Process description

Vat polymerization was first developed by Charles Hull in 1986. This process starts with a print plate being placed on the very top of a vat filled with a photo-reactive resin. A light source is then used to cure the first layer and bond it to the bottom of the plate. The plate is then raised so that the next layer is cured directly onto the last. This is repeated until the part is complete. The part then washed and further hardened with a strong light.

Strengths & Weaknesses

Strengths

High resolution and surface finish: This process has the highest resolution of all additive manufacturing technologies since detail is only limited by screen resolution
Clear parts: The material used in Vat Polymerization allows for the creation of clear parts.

Weaknesses

Toxic materials: Most materials used in Vat Polymerization are generally extremely toxic, and should be handled with care. Protective equipment should be worn, and printing should always be done with proper ventilation to protect against toxic fumes.
Weaker material properties: Resins that are used in this process tend to be brittle and not very tough.
Post processing: VP parts need to be cleaned of wet resin, and cured a second time to ensure hardness and layer bonding.
Resin degradation: Resins tend to degrade in color and strength over time, especially if exposed to environmental elements.

Machine Ranges

Vat Polymerization produces relatively small parts with the highest resolution of any technologies. Printers can be affordable, or on the more expensive side, depending on the size and quality of prints desired.

	Worst	Best
volume X/Y/Z (mm)	96/54/127	380/380/250
resolution (mm)	.05	.003
layer height (um)	25	15
price ($)	500,000	450
Weight kg	1724	5
build rate	2	12

ProX 950

Build Volume	Layer Height	Resolution	Size xyz	power	Price	Weight
1500/750/550mm	50um	.13mm	2200/1600/2260mm	1450mW	Requires Quote	907

form 3+

Build volume	Layer Height	Resolution	Size xyz	Power	Price	Weight
145/145/145mm	25um	.025mm	386/389/458mm	250mw	2,499$	17.5

Technologies

There are two main technologies used for curing resins in Vat Polymerization printing:

Digital Light Processing (DLP): This uses a projector to cast the entire image of each layer for curing at the same time. This process is fast but with the trade off of decreasing accuracy.
Stereolithography: This processes uses a laser to cure a single section of the layer at a time, similar to Powder Bed Fusion. This enables higher resolution parts, but is slower.

Navigation

References

Rosen, Stucker, and Khorasani, Additive Manufacturing Technologies, chap. 4.

“Photopolymerization - VAT, SLA, DLP, CDLP | Make.” Accessed October 6, 2023. https://make.3dexperience.3ds.com/processes/photopolymerization.

@@ Line 37: / Line 37: @@
 |500,000
 |450
+|-
+|Weight kg
+|1724
+|5
+|-
+|build rate
+|2
+|12
+|}
+[[File:ProX 950.jpg|none|thumb|[https://www.3dsystems.com/3d-printers/prox-950 ProX 950]<nowiki/>]]
+{| class="wikitable"
+!Build Volume
+!Layer Height
+! Resolution
+!Size xyz
+!power
+!Price
+!Weight
+|-
+|1500/750/550mm
+|50um
+|.13mm
+|2200/1600/2260mm
+|1450mW
+|Requires Quote
+|907
+|}[[File:Form 3+.webp|none|thumb|[https://shorturl.at/ptwAX form 3+]]]
+{| class="wikitable"
+!Build volume
+!Layer Height
+! Resolution
+!Size xyz
+!Power
+!Price
+!Weight
+|-
+|145/145/145mm
+|25um
+|.025mm
+|386/389/458mm
+|250mw
+|2,499$
+|17.5
 |}
-[[File:ProX 950.jpg|none|thumb|ProX 950<nowiki/>https://www.3dsystems.com/3d-printers/prox-950]]
-[[File:Form 3+.webp|none|thumb|form 3+https://formlabs.com/3d-printers/form-3/?&utm_source=google&utm_medium=cpc&utm_campaign=GP_US-NA-Prospecting-Search_Brand-Form_3-Brand-EN-Exact-Paid-Adwords&utm_term=&utm_content=3d_printer_formlabs_form_3&utm_device=c&_bt=427975547888&_bk=formlabs%203%203d%20printer&_bm=e&_bn=g&_bg=70348107962&gclid=CjwKCAjwyY6pBhA9EiwAMzmfwcISgTHmFvab2u0yCjq0QD4M24y33cTUMCWUkfTWXddX7U1e75SxNRoCCQsQAvD_BwE]]
 ==Technologies==
 There are two main technologies used for curing resins in Vat Polymerization printing: